酸浸及萃取对高铁铝土矿中有价元素分离特性的影响

吕国志，张廷安，赵爱春，王红星   

  1. (东北大学多金属共生矿生态化利用教育部重点实验室，辽宁沈阳〓110819)
  • 收稿日期:2014-04-30 修回日期:2014-04-30 出版日期:2013-10-15
  • 通讯作者: ZHANG Tingan
  • 作者简介:吕国志(1981-)，男，辽宁沈阳人，东北大学讲师，博士；张廷安(1960-)，男，河南周口人，东北大学教授，博士生导师.
  • 基金资助:
    国家自然科学基金资助项目(51004033，50934005，50974035，51074047)；国家高技术研究发展计划项目(2012AA062303)；中央高校基本科研业务费专项资金资助项目(N100302005).

Effects of AcidLeaching and Extraction on Separation Characteristics of Valuable Elements from HighIron Bauxite

LYU Guozhi， ZHANG Tingan， ZHAO Aichun， WANG Hongxing   

  1. (Key Laboratory of Ecological Utilization of Multimetal Intergrown Ores of Ministry of Education， Northeastern University， Shenyang 110819， China.
  • Received:2014-04-30 Revised:2014-04-30 Online:2013-10-15
  • Contact: ZHANG Tingan
  • About author:-
  • Supported by:
    -

RichHTML

0

PDF (PC)

50

摘要： 研究了在采用分步酸浸工艺处理高铁铝土矿新工艺中，低温酸浸过程主要工艺条件对矿物中铁、铝、钪等有价元素走向的影响，以及酸浸液后续萃取分离过程的特点.结果表明:低温酸浸过程可实现矿物中的铁、铝分离，在浸出温度100℃、浸出时间60min、液固质量比20∶1、搅拌速率500r/min、粒度约-55μm、硫酸质量分数20%的低温酸浸条件下，矿物中的铁和钪的浸出率可分别达到95%和50%以上，铁、铝酸浸分离系数可达到80左右；浸出液可通过多级循环后萃取的方式提取其中的钪，在适宜的萃取条件下，钪的提取效率可达99%以上.

关键词: 高铁铝土矿, 酸浸, 萃取分离, 酸浸条件, 钪提取

Abstract: The lowtemperature acid leaching and extraction performance of “twostep leaching” process for highiron bauxite were investigated. The effects of temperature， acid concentration of leaching process and acid concentration of extraction process on the separation characteristics of elements were analyzed as well. The results showed that Fe and Al in bauxite were separated by the low temperature acid leaching method， with the leaching temperature 100℃， leaching time 60min， liquidsolid ratio 20∶1， rotary speed 500r/min， particle sizes about-55μm and the acid mass fraction 20%. The leaching efficiency of Fe and Sc were above 95% and 50%， respectively， while the separation factors between Fe and Al were about 80. Through various stepwise circular and extraction treatment， the extraction rate of Sc in the leached liquid was above 99%.

Key words: highiron bauxite, acid leaching, extraction, acidleaching condition, Sc extracting