CoCrFeNi高熵合金组织演变规律及再结晶动力学

doi:10.12068/j.issn.1005-3026.2021.07.004

东北大学学报（自然科学版） ›› 2021, Vol. 42 ›› Issue (7): 933-938.DOI: 10.12068/j.issn.1005-3026.2021.07.004

CoCrFeNi高熵合金组织演变规律及再结晶动力学

毕梦园，谢仁义，张艺凡，衣海龙

(东北大学轧制技术及连轧自动化国家重点实验室，辽宁沈阳110819)

修回日期:2020-12-21 接受日期:2020-12-21 发布日期:2021-07-16
通讯作者: 毕梦园
作者简介:毕梦园(1995-)，女，江苏徐州人，东北大学硕士研究生; 衣海龙(1979-)，男，辽宁阜新人，东北大学副教授，硕士生导师.
基金资助:
国家自然科学基金资助项目(51674079).

Microstructure Evolution and Recrystallization Kinetics of CoCrFeNi High Entropy Alloy

BI Meng-yuan， XIE Ren-yi， ZHANG Yi-fan， YI Hai-long

State Key Laboratory of Rolling and Automation， Northeastern University， Shenyang 110819， China.

Revised:2020-12-21 Accepted:2020-12-21 Published:2021-07-16
Contact: YI Hai-long
About author:-
Supported by:
-

摘要/Abstract

摘要： 利用Gleeble-1500D热模拟试验机对添加少量C原子的非等原子比CoCrFeNi高熵合金进行热变形处理.结果表明，当变形温度为1123K，应变速率为0.1s^-1时，合金的显微组织主要为变形晶粒，随着温度的升高或应变速率的降低，变形晶粒边缘开始出现细小的等轴晶；当变形温度为1223K时，其组织全部为等轴的再结晶晶粒.当变形温度大于1223K时，晶粒开始出现明显的长大现象.利用Arrhenius模型及Avrami方程，建立了CoCrFeNi高熵合金的再结晶动力学模型，对应的再结晶激活能为526.078kJ·mol^-1.

关键词: 高熵合金；热变形；显微组织；再结晶动力学；激活能

Abstract: Using a Gleeble-1500D thermal simulator， the non-equal molar CoCrFeNi high entropy alloy doped with minor carbon was conducted by hot deformation under different deformation conditions. The results show that when the temperature is 1123K and strain rate is 0.1s^-1， the microstructure is mainly composed of deformed grains. With the increase of temperature or decrease of strain rate， fine grains start to appear at the deformed grains edge. When the temperature increases to 1223K， all microstructure is transformed to equiaxed recrystallization grains. When the temperature is higher than 1223K， the grains become coarse. Arrhenius model and Avrami equation were used to build the kinetic model of recrystallization， and the activation energy was obtained as 526.078kJ/mol.

Key words: high entropy alloy; hot deformation; microstructure; recrystallization kinetics; activation energy

中图分类号:

TG139

毕梦园，谢仁义，张艺凡，衣海龙. CoCrFeNi高熵合金组织演变规律及再结晶动力学[J]. 东北大学学报（自然科学版）, 2021, 42(7): 933-938.

BI Meng-yuan， XIE Ren-yi， ZHANG Yi-fan， YI Hai-long. Microstructure Evolution and Recrystallization Kinetics of CoCrFeNi High Entropy Alloy[J]. Journal of Northeastern University(Natural Science), 2021, 42(7): 933-938.

参考文献

[1]Wu Z，Bei H，Pharr G M，et al.Temperature dependence of the mechanical properties of equiatomic solid solution alloys with face-centered cubic crystal structures［J］.Acta Materialia，2014，81:428-441.
[2]Vaidya M，Guruvidyathri K，Murty B S.Phase formation and thermal stability of CoCrFeNi and CoCrFeMnNi equiatomic high entropy alloys［J］.Journal of Alloys and Compounds，2019，774:856-864.
[3]Vaidya M，Anirudha K，Marshal A，et al.Phase evolution and stability of nanocrystalline CoCrFeNi and CoCrFeMnNi high entropy alloys［J］.Journal of Alloys and Compounds，2019，770:1004-1015.
[4]Wei D，Li X，Heng W，et al.Novel Co-rich high entropy alloys with superior tensile properties［J］.Materials Research Letters，2019，7(2):82-88.
[5]Wei D，Li X，Jiang J，et al.Novel Co-rich high performance twinning-induced plasticity(TWIP) and transformation-induced plasticity(TRIP) high-entropy alloys［J］.Scripta Materialia，2019，165:39-43.
[6]Ko J Y，Hong S I.Microstructural evolution and mechanical performance of carbon-containing CoCrFeMnNi-C high entropy alloys［J］.Journal of Alloys and Compounds，2018，743:115-125.
[7]Li Z M，Tasan C C，Pradeep K G，et al.A TRIP-assisted dual-phase high-entropy alloy:grain size and phase fraction effects on deformation behavior［J］.Acta Materialia，2017，131:323-335.
[8]Sathiaraj G D，Ahmed M Z，Bhattacharjee P P.Microstructure and texture of heavily cold-rolled and annealed fcc equiatomic medium to high entropy alloys［J］.Journal of Alloys and Compounds，2016，664:109-119.
[9]He G A，Zhao Y F，Gan B，et al.Mechanism of grain refinement in an equiatomic medium-entropy alloy CrCoNi during hot deformation［J］.Journal of Alloys and Compounds，2020，815:152382.
[10]Wang J，Liu Y，Liu B，et al.Flow behavior and microstructures of powder metallurgical CrFeCoNiMo_0.2 high entropy alloy during high temperature deformation［J］.Materials Science and Engineering:A，2017，689:233-242.
[11]Tsai K Y，Tsai M H，Yeh J W.Sluggish diffusion in Co-Cr-Fe-Mn-Ni high-entropy alloys［J］.Acta Materialia，2013，61(13):4887-4897.
[12]Eleti R R，Bhattacharjee T，Zhao L，et al.Hot deformation behavior of CoCrFeMnNi FCC high entropy alloy［J］.Materials Chemistry and Physics，2017，210:176-186.
[13]Nayan N，Singh G，Murty S V S N，et al.Hot deformation behaviour and microstructure control in AlCrCuNiFeCo high entropy alloy［J］.Intermetallics，2014，55:145-153.
[14]Li J，Gao B，Tang S，et al.High temperature deformation behavior of carbon-containing FeCoCrNiMn high entropy alloy［J］.Journal of Alloys and Compounds，2018，747:571-579.
[15]周金莲.Al_0.6CoCrFeNi双相高熵合金的热变形行为及组织调控［D］.北京:北京理工大学，2016.(Zhou Jin-lian.Hot deformation behavior and microstructure control in dual-phase Al_0.6CoCrFeNi high entropy alloy［D］.Beijing:Beijing Institute of Technology，2016.)
[16]Kahnooji M，Hanzaki A Z，Abedi H R，et al.An investigation into the dynamic recrystallization behavior of a non-equiatomic high entropy alloy［J］.Materials Science and Engineering:A，2019，768:138423.
[17]Annasamy M，Haghdadi N，Taylor A，et al.Dynamic recrystallization behaviour of AlxCoCrFeNi high entropy alloys during high-temperature plane strain compression［J］.Materials Science and Engineering:A，2019，745:90-106.
[18]Bergstrm Y.A dislocation model for the stress-strain behaviour of polycrystalline α-Fe with special emphasis on the variation of the densities of mobile and immobile dislocations［J］.Materials Science and Engineering，1970，5(4):193-200.

CoCrFeNi高熵合金组织演变规律及再结晶动力学

Microstructure Evolution and Recrystallization Kinetics of CoCrFeNi High Entropy Alloy

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 2

编辑推荐

Metrics

本文评价

[1]	白静，杨禛，赵晨羽，赵骧. NiMnGaTi铁磁形状记忆合金的马氏体相变和磁性能[J]. 东北大学学报:自然科学版, 2019, 40(10): 1398-1402.
[2]	高淑春，翟玉春，姜妲，王秋实. 活化溅射法在NiTi合金上制备TiO2生物薄膜[J]. 东北大学学报(自然科学版), 2013, 34(6): 859-862.