SCR废催化剂中钒和钨常温常压浸出新工艺

刘娜娜，徐新阳，陈熙，刘源

(东北大学资源与土木工程学院，辽宁沈阳110819)

修回日期:2021-07-23 接受日期:2021-07-23 发布日期:2022-05-18
通讯作者: 刘娜娜
作者简介:刘娜娜(1990-)，女，河北沧州人，东北大学博士研究生; 徐新阳(1967-)，男，浙江武义人，东北大学教授，博士生导师.
基金资助:
国家重点研发计划项目(ZX20200121).

Novel Leaching Process of Vanadium and Tungsten from Spent SCR Catalyst at Normal Temperature and Pressure

LIU Na-na， XU Xin-yang， CHEN Xi， LIU Yuan

School of Resources & Civil Engineering， Northeastern University， Shenyang 110819， China.

Revised:2021-07-23 Accepted:2021-07-23 Published:2022-05-18
Contact: XU Xin-yang
About author:-
Supported by:
-

摘要/Abstract

摘要： 基于SEM-EDS，XPS，获得常温常压下SCR废催化剂二段式浸出新工艺，采用Box-Behnken试验设计(BBD)方法分段研究了各因素及其交互作用对钒和钨浸出影响，得到了最佳工艺参数，并分析了浸出机理.结果表明，采用二段式浸出工艺，各因素影响顺序为:第一阶段提钒，反应温度＞浸出时间＞浸出剂浓度;第二阶段提钨，反应温度＞浸出剂浓度＞浸出时间.第一段当NaOH浓度0.5mol·L^-1，60℃下反应10min时，钒浸出率为(61.40±0.24)%;第二段当NaOH浓度2.5mol·L^-1，90℃下反应50min时，钨浸出率为(55.73±0.22)%.废催化剂中钒以V₂O₃，VOSO₄和V₂O₅形式存在，与NaOH反应生成可溶性钒酸盐，少部分V₂O₃和V₂O₅在反应过程中生成VOSO₄后溶解.

关键词: SCR废催化剂;Box-Behnken试验设计;SEM-EDS;XPS

Abstract: Based on SEM-EDS and XPS， a novel two-stage leaching process of spent SCR(selective catalytic reduction) catalyst under normal temperature and pressure was proposed. Box-Behnken design(BBD)was used to study the effects of various factors and their interactions on the leaching of vanadium and tungsten， then，the optimal process parameters were obtained and the leaching mechanism was studied. The results showed that: during the two-stage leaching process， the order of influence factors on the leaching rate is temperature >time>leaching agent concentration in the first stage(vanadium extraction process) and temperature>leaching agent concentration>time in the second stage(tungsten extraction process). In the first stage， when the NaOH concentration is 0.5mol·L^-1and reacts at 60℃ for 10min， the vanadium leaching rate is(61.40±0.24)%. In the second stage， when the NaOH concentration is 2.5mol·L^-1and reacts at 90℃ for 50min， the tungsten leaching rate is(55.73±0.22)%. Vanadium in the spent catalyst exists in the form of V₂O₃， VOSO₄ and V₂O₅， and reacts with NaOH to form soluble vanadate. A small part of V₂O₃ and V₂O₅ are dissolved after forming VOSO₄.

Key words: spent SCR catalyst; Box-Behnken design; SEM-EDS; XPS

中图分类号:

X705

刘娜娜，徐新阳，陈熙，刘源. SCR废催化剂中钒和钨常温常压浸出新工艺[J]. 东北大学学报（自然科学版）, 2022, 43(3): 414-423.

LIU Na-na， XU Xin-yang， CHEN Xi， LIU Yuan. Novel Leaching Process of Vanadium and Tungsten from Spent SCR Catalyst at Normal Temperature and Pressure[J]. Journal of Northeastern University(Natural Science), 2022, 43(3): 414-423.

参考文献

[1]Topsoe N Y，Dumesic J A，Topsoe H.Vanadia-titania catalysts for selective catalytic reduction of nitric-oxide by ammonia.Ⅱ.studies of active-sites and formulation of catalytic cycles［J］.Journal of Catalysis，1995，151(1):241-252.
[2]陈颖敏，谢宗，王超凡.燃煤电厂废弃SCR催化剂回收二氧化钛的研究［J］.中国电力，2016，49(6):151-156.(Chen Ying-min，Xie Zong，Wang Chao-fan.Study on TiO₂ recovery from SCR catalyst waste in coal-fired power plants［J］.Electric Power，2016，49(6):151-156.)
[3]Huo Y T，Chang Z，Li W，et al.Reuse and valorization of vanadium and tungsten from waste V₂O₅-WO₃/TiO₂ SCR catalyst［J］.Waste and Biomass Valorization，2015，6(2):159-165.
[4]Ma B T，Qiu Z F，Yang J，et al.Recovery of nano-TiO₂ from spent SCR catalyst by sulfuric acid dissolution and direct precipitation［J］.Waste and Biomass Valorization，2019，10(10):3037-3044.
[5]Zhang Q，Wu Y，Li L，et al.Sustainable approach for spent V₂O₅-WO₃/TiO₂ catalysts management:selective recovery of heavy metal vanadium and production of value-added WO₃-TiO₂ photocatalysts［J］.ACS Sustainable Chemistry & Engineering，2018，6(9):12502-12510.
[6]Choi I，Moon G，Lee J，et al.Hydrometallurgical processing of spent selective catalytic reduction(SCR)catalyst for recovery of tungsten［J］.Hydrometallurgy，2018，178:137-145.
[7]Kim J W，Lee W G，Hwang I S，et al.Recovery of tungsten from spent selective catalytic reduction catalysts by pressure leaching［J］.Journal of Industrial and Engineering Chemistry，2015，28:73-77.
[8]Kim J W，Hwang I.Separation of valuables from spent selective catalytic reduction catalyst leaching solution by fabricated anion extraction resins［J］.Journal of Environmental Chemical Engineering，2018，6(1):1100-1108.
[9]Khuri A I，Mukhopadhyay S.Response surface methodology［J］.Wiley Interdisciplinary Reviews:Computational Statistics，2010，2(2):128-149.
[10]Krishnan S，Zulkapli N S，Din M，et al.Statistical optimization of titanium recovery from drinking water treatment residue using response surface methodology［J］.Journal of Environmental Management，2020，255:109890.1-109890.9.
[11]Liu N，Xu X，Liu Y.Recovery of vanadium and tungsten from spent selective catalytic reduction catalyst by alkaline pressure leaching［J］.Physicochemical Problems of Mineral Processing，2020，56(3):407-420.
[12]Wang C，Yang S，Chang H，et al.Dispersion of tungsten oxide on SCR performance of V₂O₅-WO₃/TiO₂:acidity，surface species and catalytic activity［J］.Chemical Engineering Journal，2013，225:520-527.
[13]Su Q F，Miao J F，Li H R，et al.Optimizing vanadium and tungsten leaching with lowered silicon from spent SCR catalyst by pre-mixing treatment［J］.Hydrometallurgy，2018，181:230-239.
[14]Zhang S L，Zhong Q.Surface characterization studies on the interaction of V₂O₅-WO₃/TiO₂ catalyst for low temperature SCR of NO with NH₃［J］.Journal of Solid State Chemistry，2015，221:49-56.
[15]Shen M Q，Li C X，Wang J Q，et al.New insight into the promotion effect of Cu doped V₂O₅/WO₃-TiO₂ for low temperature NH₃-SCR performance［J］.RSC Advances，2015，5(44):35155-35165.

SCR废催化剂中钒和钨常温常压浸出新工艺

Novel Leaching Process of Vanadium and Tungsten from Spent SCR Catalyst at Normal Temperature and Pressure

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 8

编辑推荐

Metrics

本文评价

[1]	程云虹，黄菲，齐珊珊，李文川. 高硅型铁尾矿对混凝土碳化及抗硫酸盐腐蚀性能的影响[J]. 东北大学学报:自然科学版, 2019, 40(1): 121-126.
[2]	由美雁，张秀秀，沈阳，朱彤. 超声空化热效应破解剩余污泥的机制[J]. 东北大学学报:自然科学版, 2019, 40(1): 126-131.
[3]	谢元华，梅健，王杰，朱彤. 爆炸冲击波破解剩余污泥的实验研究[J]. 东北大学学报:自然科学版, 2018, 39(3): 446-450.
[4]	李现瑾，苑春莉，余宏，朱彤. 厌氧处理结合超声空化高效破解剩余污泥[J]. 东北大学学报:自然科学版, 2015, 36(6): 868-872.
[5]	由美雁，李现瑾，王利伟，朱彤. 超声破解剩余污泥的研究[J]. 东北大学学报:自然科学版, 2014, 35(3): 447-451.
[6]	何丽莉，徐新阳. 煤矸石酸溶法制得聚合氯化铝铁钙的形态[J]. 东北大学学报(自然科学版), 2013, 34(10): 1477-1480.
[7]	程云虹，黄菲，李光禄，秦志生. 陶泥的活性评价及其对混凝土抗压强度的影响[J]. 东北大学学报(自然科学版), 2013, 34(10): 1499-1503.
[8]	谢元华，杨岱恩，白冰，朱彤. 高压喷射撞击流破解剩余污泥的研究[J]. 东北大学学报（自然科学版）, 2021, 42(12): 1790-1796.