后桥主减速器壳体轴承座的裂解加工数值分析

金文明1, 姚娟2, 赵勇1, 郭贝贝2   

  1. (1. 吉林大学 辊锻工艺研究所, 吉林 长春130022; 2. 吉林大学 材料科学与工程学院, 吉林 长春130022)
  • 收稿日期:2017-05-09 修回日期:2017-05-09 出版日期:2018-09-15 发布日期:2018-09-12
  • 通讯作者: 金文明
  • 作者简介:金文明(1962-),男,黑龙江齐齐哈尔人,吉林大学副教授.冯明杰(1971-), 男, 河南禹州人, 东北大学副教授; 王恩刚(1962-), 男, 辽宁沈阳人, 东北大学教授,博士生导师.
  • 基金资助:
    国家科技重大专项 (2013ZX04002021).国家自然科学基金资助项目(51171041).

Numerical Analysis of Fracture Splitting Technology of Rear Axles’ Main Reducer Shell Bearing Seats

JIN Wen-ming1, YAO Juan2, ZHAO Yong1, GUO Bei-bei2   

  1. 1.Roll Forging Technology Research Institute, Jilin University, Changchun 130022, China; 2. School of Materials Science and Engineering, Jilin University, Changchun 130022,China.
  • Received:2017-05-09 Revised:2017-05-09 Online:2018-09-15 Published:2018-09-12
  • Contact: YAO Juan
  • About author:-
  • Supported by:
    -

摘要: 利用ABAQUS 模拟后桥主减速器壳体轴承座的启裂并进行数值分析.壳体轴承座材料选用基体组织中珠光体体积分数50%的QT450,通过J积分确定了启裂点位置,计算出裂解载荷;分析了启裂时裂尖区域的塑性变形及其对轴承孔失圆量的影响,并进行了实验研究.结果表明,壳体轴承座的启裂点位于靠近裂尖中部位置;塑性区域位于裂尖根部呈蝶形分布,造成的轴承孔失圆度较小;裂解加工质量合格,说明轴承座适合使用裂解技术.研究结果为改进壳体轴承座的生产工艺流程奠定了坚实的理论基础,为壳体轴承座裂解材料的选择、裂解设备的设计、工艺过程的制定提供了参考.

关键词: 壳体轴承座, QT450, 裂解加工, J积分, 数值分析

Abstract: The initial fracture splitting process of rear axles’ main reducer shell bearing seats was simulated by ABAQUS and a numerical analysis was carried out. The material of the shell bearing seats is QT450 with 50% pearlite in the matrix structure. The position of the starting cracking point was determined by J integral, and the splitting force was then calculated. The plastic deformation of the crack tip region when cracking and its effect on the loss of circle were analyzed, and an experimental study was conducted. The results show that the starting cracking point of the bearing is located near the middle of the crack tip. The plastic area located at the root of the crack tip is of butterfly-shaped distribution, resulting in the small loss of circle of bearing holes. The processing quality of fracture splitting is qualified, which is suitable for the application of fracture splitting technology.The research result lays a solid theoretical foundation for improving the production process of shell bearing seats, and provides a reference for the selection of splitting materials of shell bearing seats, the design of splitting equipment and the formulation of processing procedures.

Key words: shell bearing seat, QT450, fracture splitting process, J integral, numerical analysis