Foaming parameters and quasi-static compressibility of Al foams made by PM route

Wang, Lei (1); Yao, Guang-Chun (1); Zhang, Xiao-Ming (1); Zu, Guo-Yin (1)   

  1. (1) School of Materials and Metallurgy, Northeastern University, Shenyang 110004, China
  • Received:2013-06-20 Revised:2013-06-20 Online:2010-02-15 Published:2013-06-20
  • Contact: Yao, G.-C.
  • About author:-
  • Supported by:
    -

RichHTML

0

PDF (PC)

732

摘要： 利用粉末冶金法成功制备出不同表观密度的铝基泡沫材料,详细探讨了发泡工艺参数对泡孔结构和膨胀行为的影响.结果显示:前驱体自身温度变化分为线性快速升温、温度恒定和快速冷却三个阶段,发泡炉温的选择取决于线性快速升温阶段;比较不同发泡时间的泡孔结构和膨胀行为,可以得出最佳发泡时间和膨胀率分别为120 s和434%;前驱体预热对前驱体升温速率影响不大,但是可以缩短发泡时间.准静态压缩实验结果显示:铝基泡沫材料坍塌阶段的应力没有明显的波动,压缩强度、弹性模量以及压实应变都随着表观密度的增加而增加.

关键词: 泡沫铝, 粉末冶金, 发泡工艺参数, 表观密度, 压缩强度

Abstract: Aluminum (Al) foams with different apparent densities were prepared successfully by powder metallurgy (PM) route. The effects of foaming process parameters on cell structures and expansion behavior were discussed in detail. The results showed that the temperature variation of foamable precursors is divided into three phases, i.e., linearly quick rising, constant and quick cooling, and the choice of furnace temperature depends on the linearly quick rising. The optimum foaming time and expansion rate are 120 sec and 434%, respectively, through the comparison of the cell structures and expansion behavior at different foaming times. Preheating precursors does not affect their temperature rising rates obviously but shortens the foaming time. The results of quasi-static compressibility tests showed that no obvious stress fluctuation is found during the collapse process of Al foams and the compressive strength, elastic modulus and compact stress all increase with apparent density.