退火方式对含硼冷轧深冲搪瓷钢组织性能的影响

董福涛1，杜林秀1，刘相华1，薛飞2   

  1. (1.东北大学轧制技术及连轧自动化国家重点实验室，辽宁沈阳110819；2.河北联合大学电气工程学院，河北唐山063000)
  • 收稿日期:2013-03-12 修回日期:2013-03-12 出版日期:2013-10-15 发布日期:2013-05-24
  • 通讯作者: 董福涛
  • 作者简介:董福涛(1985-)，男，河北唐山人，东北大学博士研究生；杜林秀(1962-)，男，辽宁本溪人，东北大学教授，博士生导师；刘相华(1953-)，男，黑龙江双鸭山人，东北大学教授，博士生导师.
  • 基金资助:
    国家重点基础研究发展计划项目(2011CB606306-2).

Effect of Annealing Modes on Microstructure and Properties of Boron Containing ColdRolled DeepDrawing Enamel Steel

DONG Futao1， DU Linxiu1， LIU Xianghua1， XUE Fei2   

  1. 1. State Key Laboratory of Rolling and Automation， Northeastern University， Shenyang 110819， China; 2. College of Electrical Engineering， Hebei United University， Tangshan 063000， China.
  • Received:2013-03-12 Revised:2013-03-12 Online:2013-10-15 Published:2013-05-24
  • Contact: DU Linxiu
  • About author:-
  • Supported by:
    -

RichHTML

1

PDF (PC)

658

摘要： 在实验室条件下研究了罩式退火和快速连续退火两种方式对含硼搪瓷钢微观组织、力学性能和抗鳞爆性能的影响.结果表明:适当增加Mn，S的质量分数和添加微量B，实验钢不同方式退火板的性能均较好；连续退火板强度稍高于罩式退火板，伸长率A50和rm值明显高于罩式退火板，综合力学性能较好；连续退火板的氢扩散速率明显小于罩式退火板，主要得益于采用快速连续退火得到的实验钢中铁素体晶粒内存在大量弥散分布的渗碳体颗粒作为有效氢陷阱；采用快速连续退火可以实现含硼搪瓷钢良好的力学性能和抗鳞爆性能的匹配.

关键词: 搪瓷钢, 快速连续退火, 渗碳体, 微量硼, 抗鳞爆性能

Abstract: The effect of two annealing modes (batch annealing and rapid continuous annealing) on the microstructure， mechanical properties and fishscale resistance of boron containing enamel steel was investigated. The results showed that appropriately increasing the mass fraction of Mn， S and adding trace boron， both the tested steel sheets under the two annealing modes had good properties. The strength of the continuous annealed sheet was slightly higher， and the elongation A50 and rmvalues of the continuous annealed sheet were apparently higher than that of the batch annealed sheet. The continuous annealed sheet showed better comprehensive mechanical properties. The hydrogen diffusion rate in the continuous annealed sheet was much lower than that in the batch annealed sheet. This was mainly attributed to large amount of dispersed cementite particles precipitate within ferrite grains which can act as effective hydrogen traps in the ultrafast continuous annealing steels. The match of good mechanical properties with fishscale resistance of the boron contained enamel steel was realized through rapid continuous annealing process.

Key words: enamel steels, rapid continuous annealing, cementite, trace boron, fishscale resistance