含硼铁精矿用于巴润精矿氧化球团生产的实验研究

付小佼， 储满生   

  1. (东北大学 材料与冶金学院， 辽宁 沈阳110819)
  • 收稿日期:2013-11-28 修回日期:2013-11-28 出版日期:2015-01-15 发布日期:2014-11-07
  • 通讯作者: 付小佼
  • 作者简介:付小佼(1989-)，女，山东潍坊人，东北大学博士研究生； 储满生(1973-)，男，安徽岳西人，东北大学教授，博士生导师.
  • 基金资助:
    教育部高等学校博士学科点专项科研基金资助项目(20100042110004)； 中央高校基本科研业务费专项资金资助项目(N090502004).

Experimental Study on Preparation of Oxidized Barun Iron Ore Pellets with Boron-Bearing Iron Concentrate Addition

FU Xiao-jiao， CHU Man-sheng   

  1. School of Materials & Metallurgy， Northeastern University， Shenyang 110819， China.
  • Received:2013-11-28 Revised:2013-11-28 Online:2015-01-15 Published:2014-11-07
  • Contact: CHU Man-sheng
  • About author:-
  • Supported by:
    -

RichHTML

0

PDF (PC)

826

摘要： 在实验室条件下，研究了含硼铁精矿对巴润精矿氧化球团制备工艺及冶金性能的影响.研究表明:球团原料中外配5.0%的含硼铁精矿，可将混合料中的巴润精矿配比(质量分数)提高到40%，制备的氧化球团满足高炉冶炼要求;含硼铁精矿可增加巴润精矿氧化球团的抗压强度和降低还原膨胀率，并可降低球团的焙烧温度;当含硼铁精矿配加量(质量分数)从0增加到7.5%时，球团抗压强度从2630N·个-1上升到3709N·个-1，还原膨胀率从25.69%降低到15.53%;外配质量分数为7.5%的含硼铁精矿时，球团的焙烧温度可从1200℃降低至1150℃，巴润精矿氧化球团满足高炉生产要求.

关键词: 高碱负荷铁矿, 巴润精矿, 含硼铁精矿, 氧化球团, 冶金性能

Abstract: Under laboratory conditions， experiments on the effect of boron-bearing iron concentrate on the preparation process and metallurgical properties of oxidized Barun iron ore pellets were carried out. The results show that， when the additional addition of boron-bearing iron concentrate is 5.0%， the oxidized iron ore pellets with 40% Barun iron ore content can meet the requirements of blast furnace smelting. Boron-bearing iron concentrate can increase the crushing strength of pellets and decrease the reduction swelling rate. With increasing the additional addition of boron-bearing iron concentrate from 0 to 7.5%， the crushing strength is raised from 2630 N to 3709N， the reduction swelling rate is decreased from 25.69% to 15.53%. When the additional addition of boron-bearing iron concentrate is 7.5%， the pellets roasting temperature can be decreased from 1200℃ to 1150℃， and the quality of the oxidized Barun iron ore pellets can still meet the requirements of blast furnace smelting.

Key words: iron ore concentrate with high alkalis load, Barun iron ore, boron-bearing iron concentrate, pellets, metallurgical properties