中性气氛下钒钛磁铁矿高炉渣系研究

储满生， 冯聪， 唐珏， 柳政根   

  1. (东北大学 材料与冶金学院， 辽宁 沈阳110819)
  • 收稿日期:2014-07-21 修回日期:2014-07-21 出版日期:2015-09-15 发布日期:2015-09-14
  • 通讯作者: 储满生
  • 作者简介:储满生(1973-)，男，安徽岳西人，东北大学教授，博士生导师.
  • 基金资助:
    国家自然科学基金重大资助项目(51090384)；国家高技术研究发展计划项目(2012AA062302)；中央高校基本科研业务费专项资金资助项目(N130602003).

Study on Blast Furnace Slag System of Vanadium-Titanium Magnetite Under Neutral Atmosphere

CHU Man-sheng， FENG Cong， TANG Jue， LIU Zheng-gen   

  1. School of Materials & Metallurgy， Northeastern University， Shenyang 110819， China.
  • Received:2014-07-21 Revised:2014-07-21 Online:2015-09-15 Published:2015-09-14
  • Contact: CHU Man-sheng
  • About author:-
  • Supported by:
    -

RichHTML

0

PDF (PC)

689

摘要： 以钒钛磁铁矿现场高炉渣为基础，纯化学试剂调制渣样，在中性气氛条件下研究了炉渣二元碱度及MgO，Al2O3，TiO2，V2O5含量对实验渣系冶金性能的影响.结果表明:增加碱度和MgO含量，炉渣熔化性温度(t○m)、初始黏度(η○0)和高温黏度(η○h)呈先降低后升高趋势；增大Al2O3含量，炉渣tm升高，η○0先降低后升高，η○h呈上升趋势；增大TiO2含量，炉渣t○m升高，η○0和η○h逐渐下降，炉渣黏流活化能升高，热稳定性变差；增大V2O5含量，炉渣t○m先降低后升高，η○0和η○h逐渐增大.高炉冶炼钒钛磁铁矿适宜渣系为:二元碱度 1.15，MgO，Al2O3，TiO2，V2O5质量分数分别为13%，13%，7%，0.30%.

关键词: 钒钛磁铁矿, 高炉渣, 炉渣成分, 冶金性能, 中性气氛

Abstract: The components of practical blast furnace (BF) slag of vanadium-titanium magnetite were adjusted by adding pure chemical reagents. The effects of binary basicity， MgO， Al2O3， TiO2 and V2O5 on the metallurgical properties of experimental slag were studied under neutral atmosphere. The results showed that with increasing content of basicity and MgO， the melting temperature (t○m)， initial viscosity (η○0) and high-temperature viscosity (η○h) of slag first decrease and then increase. As increasing Al2O3 content， t○m increases， η○0 first decreases and then increases， η○h increases. When increasing TiO2 content， t○m increases， η○0 and η○h decrease. The viscosity flow activation energy of slag increases and the heat stability of slag becomes worse. With increasing V2O5 content， t○m first decreases and then increases， η○0 and η○h increase. The suitable BF slag for smelting vanadium-titanium magnetite is: binary basicity 1.15，MgO 13%， Al2O3 13%， TiO2 7%，V2O5 0.30%.

Key words: vanadium-titanium magnetite, blast furnace slag, slag component, metallurgical properties, neutral atmosphere