铝热自蔓延制备CuCr合金渣系粘度测量及模型建立(Ⅱ)

张廷安;豆志河;徐淑香;杨欢   

  1. 东北大学材料与冶金学院;东北大学材料与冶金学院;中国铝业集团;东北大学材料与冶金学院 辽宁沈阳　110004
  • 收稿日期:2013-06-24 修回日期:2013-06-24 出版日期:2004-02-15 发布日期:2013-06-24
  • 通讯作者: Zhang, T.-A.
  • 作者简介:-
  • 基金资助:
    国家自然科学基金资助项目(59971016,50374026)

Viscosity measurement and modeling of slag systems of CuCr alloys prepared through Al thermit-SHS (II)

Zhang, Ting-An (1); Dou, Zhi-He (1); Xu, Shu-Xiang (2); Yang, Huan (1)   

  1. (1) Sch. of Mat. and Metall., Northeastern Univ., Shenyang 110004, China; (2) Aluminium Co. of China, Beijing 100088, China
  • Received:2013-06-24 Revised:2013-06-24 Online:2004-02-15 Published:2013-06-24
  • Contact: Zhang, T.-A.
  • About author:-
  • Supported by:
    -

RichHTML

0

PDF (PC)

479

摘要： 用已建立的针对非二氧化硅体系的粘度模型对CaO Al2O3体系的粘度值进行估算,与前人的测量值进行了比较,估算值和文献测量值吻合·根据已知文献确定了CaO Al2O3体系中的Al3+和Ca2+的离子作用系数L·由测量知,CaO Al2O3体系共晶点附近的熔渣流动性好,在1460℃时粘度值低于0 5Pa·s·对于Al2O3 CaO MgO体系按两个不同共晶点处的成分配渣,其中含氧化钙较多的渣粘度较低,1500℃时,其粘度小于0 03Pa·s·添加剂MgO能显著降低CaO Al2O3体系的熔渣粘度·

关键词: 触头材料, 铝热反应, CuCr合金, 粘度, 熔渣, 添加剂

Abstract: The viscosity model, which has already been built to apply as a reference to the slag systems without SiO2, was used to estimate the viscosities of Al2O3-CaO system. The results showed that the estimated values conform well with the measured values as shown in some known literatures. The ionization factor, L, between A13+ and Ca2+ in the Al2O3-CaO system was determined from the experimental data as shown in known literatures. According to the measurements, the slags have good fluidities around the eutectic point and the viscosities are below 0.5 Pa·s at 1460°C for Al2O3-CaO system. As to Al2O3-CaO-MgO system, the slags were prepared according to compositions of two different eutectic points, and the viscosity of the slag which contains more CaO is lower, ie. lower than 0.03 Pa·s at 1500°C. In addition, the additive MgO can reduce obviously the slag viscosity values of Al2O3-CaO system.