东北大学学报:自然科学版 ›› 2015, Vol. 36 ›› Issue (8): 1150-1154.DOI: 10.12068/j.issn.1005-3026.2015.08.019

• 材料与冶金 • 上一篇    下一篇

含氟及手性交联剂的液晶弹性体的合成与性能

何晓智， 於飞飞， 宋紫艳， 胡建设   

  1. (东北大学 理学院， 辽宁 沈阳110819)
  • 收稿日期:2014-05-28 修回日期:2014-05-28 出版日期:2015-08-15 发布日期:2015-08-28
  • 通讯作者: 何晓智
  • 作者简介:何晓智 (1969-)，女，辽宁抚顺人，东北大学副教授； 胡建设(1971-)，男，河南周口人，东北大学教授，博士生导师.
  • 基金资助:
    国家自然科学基金资助项目(21273035)； 中央高校基本科研业务费专项资金资助项目(N110705001)；辽宁省自然科学基金资助项目(201102061).

Synthesis and Properties of Liquid Crystal Elastomers Containing Fluorine and Chiral Crosslinking Agent

HE Xiao-zhi， YU Fei-fei， SONG Zi-yan， HU Jian-she   

  1. School of Sciences， Northeastern University， Shenyang 110819， China.
  • Received:2014-05-28 Revised:2014-05-28 Online:2015-08-15 Published:2015-08-28
  • Contact: HE Xiao-zhi
  • About author:-
  • Supported by:
    -

RichHTML

0

PDF (PC)

524

摘要： 合成向列液晶单体:4-((4-烯丙氧基)苯甲酰氧基)苯基-4-氟苯甲酸)酯(M1)和非液晶手性交联剂:双(4-((4－烯丙氧基)苯甲酰氧基)异山梨醇酯)(MC).按不同比例将M1和MC接枝共聚到聚甲基含氢硅氧烷上，得到含氟手性液晶弹性体PI~PVIII.用红外光谱、核磁共振表征单体和聚合物结构，用差示扫描量热仪、热失重仪、偏光显微镜及X射线衍射等手段研究其液晶性能.结果表明，含氟类短而硬的液晶基元更易被手性诱导，出现性能优异的胆甾相.其中，PI为向列型液晶，PII~PVII为出现油丝和Grandjean织构的胆甾型液晶，PVIII没有液晶性.弹性体玻璃化转变温度随着手性交联剂含量的增加先增大后减小，熔点和清亮点均呈下降趋势.所合成的液晶弹性体热稳定性好，质量损失5%时的热失重温度均在300℃以上.

关键词: 手性, 胆甾, 含氟, 弹性体, Grandjean蓝

Abstract: Nematic monomer: 4-(4-(allyloxy)benzoyloxy)phenyl 4-fluorobenzoate (M1) and non-liquid crystalline crosslinking agent: bis((4-(4-allyloxy)benzoyloxy)isosorbide benzoate)(MC) were synthesized. M1 and MC with different proportions reacted with polymethylhydrosiloxane and chiral liquid crystalline elastomers containing fluorine PI-PVIII were got. The chemical structures and mesomorphic properties of monomers and elastomers were studied by means of FT-IR， 1H NMR， POM， DSC， TGA and X-ray. The experiment results showed that short-hard liquid crystal elements containing fluorine could be induced into cholesteric phase with wonderful properties. PI presented nematic phase and PII-PVII displayed cholesteric phase with oily-streak and Grandjean texture. PVIII did not have any liquid crystalline properties. The glass-transition temperature increased first and then decreased， whereas both the melting point and clearing point decreased. The synthesized liquid crystal elastomers had good thermal stability， and the thermal weight loss temperature was greater than 300℃ with only 5% weight lost.

Key words: chiral, choleateric, fluorine-contained, elastomer, Grandjean blue