成型压力和掺杂对Na_(1.4)Co_2O_4基材料性能的影响

厉英;马北越;姜茂发;王臻明;   

  1. 东北大学材料与冶金学院;首秦金属材料有限公司炼钢部;
  • 收稿日期:2013-06-19 修回日期:2013-06-19 发布日期:2013-04-04
  • 通讯作者: -
  • 作者简介:-
  • 基金资助:
    国家自然科学基金资助项目(51074038)

Effects of forming pressure and doping on the properties of Na1.4Co2O4-based materials

Li, Ying (1); Ma, Bei-Yue (1); Jiang, Mao-Fa (1); Wang, Zhen-Ming (2)   

  1. (1) School of Materials and Metallurgy, Northeastern University, Shenyang 110819, China; (2) Steel-Making Department, Shouqin Metal Materials Co. Ltd., Qinhuangdao 066000, China
  • Received:2013-06-19 Revised:2013-06-19 Published:2013-04-04
  • Contact: Li, Y.
  • About author:-
  • Supported by:
    -

RichHTML

0

PDF (PC)

621

摘要： 采用溶胶-凝胶法制备了Na位掺杂Sr和Li(掺杂量分别为0.1,0.2,0.3和0.4)的Na1.4Co2O4基热电材料,研究了成型压力和掺杂对Na1.4Co2O4基材料电导率、Seebeck系数和功率因子等热电性能的影响.采用XRD分析了NaxCo2O4基热电材料的相组成.研究结果表明:掺杂Sr和Li制备的Na1.4Co2O4基材料的主晶相均为γ-Na1.4Co2O4;增加成型压力及掺杂Li均可明显提高材料的电导率、Seebeck系数和功率因子;当Li掺杂量为0.4时,在310 MPa下制备的Na1.4Co2O4基材料的功率因子为7.44 mW.m-1.K-2,明显高于未掺杂试样;适量掺杂S...

关键词: 热电材料, 氧化物, 热电性能, 成型压力, 掺杂

Abstract: Na1.4Co2O4-based thermoelectric materials were prepared by sol-gel method, where the Na-site doping was done separately with Sr and Li in different amounts of 0.1, 0.2, 0.3 and 0.4. The effects of forming pressure and doping on the thermoelectric properties of the materials were investigated, such as the electric conductivity, Seebeck coefficient and power factor. The phase composition of the materials was analyzed by XRD. The results showed that the principal crystalline phase of the prepared Sr/Li-doped Na1.4Co2O4-based materials is γ-Na1.4Co2O4. The electric conductivity, Seebeck coefficient and power factor of the materials can all be increased obviously by increasing the forming pressure and Li-doping. When the doping amount of Li is 0.4, the power factor of the materials prepared under 310 MPa comes up to 7.44 mW·m-1·K-2, which is much higher than that of the materials without doping. The thermoelectric properties of Na1.4Co2O4-based materials can also be improved to a certain extent by Sr-doping in proper amount.