Texture Evolution of High Silicon Steel Ultra-thin Sheets During Cold Rolling

LIU Jin-long， SHA Yu-hui， SHAO Guang-shuai， ZOU Liang   

  1. Key Laboratory for Anisotropy and Texture of Materials， Ministry of Education， Northeastern University， Shenyang 110819， China.
  • Received:2015-12-10 Revised:2015-12-10 Online:2017-05-15 Published:2017-05-11
  • Contact: SHA Yu-hui
  • About author:-
  • Supported by:

    -

RichHTML

0

PDF (PC)

952

摘要：

采用轧制工艺制备了0.10mm厚的6.5%Si高硅电工钢超薄带，并用X射线衍射技术对冷轧过程中的形变织构演变规律进行了研究，进而提出了分别有利于λ(<100>//ND，ND为轧面法线方向)和η(<100>//RD，RD为轧向)再结晶织构优化的形变织构控制方法.研究表明，50%~70%压下率有利于η再结晶织构优化，易于促进S=0.5层强η再结晶织构的形成.小于30%压下率和91%~97%压下率均有利于λ再结晶织构优化，其中30%的压下率更适合于二次冷轧法制备高硅钢超薄带时λ再结晶织构控制.

关键词: Fe-6.5%Si, 高硅钢, 薄带, 冷轧, 织构

Abstract:

High silicon electrical steel ultra-thin sheets of 0.10mm thick， containing about 6.5% Si， were prepared by rolling method. The evolution of deformation texture during cold rolling was studied using X-ray diffraction. Then the methods of controlling deformation texture were proposed in favor of the λ (<100>//ND， normal direction) and η (<100>//RD， rolling direction) recrystallization texture， respectively. The rolling reduction between 50% and 70% is easy to promote the formation of the η recrystallization texture at the layer of S=0.5. While， the rolling reductions of either less than 30% or 91%~97% are in favor of λ recrystallization texture， in which the former reduction is more suitable to control the λ recrystallization texture when using a two-stage cold rolling method to prepare high silicon steel ultra-thin sheets.

Key words: Fe-6.5%Si, high silicon steel, thin sheets, cold rolling, texture