东北大学学报:自然科学版 ›› 2014, Vol. 35 ›› Issue (10): 1404-1407.DOI: 10.12068/j.issn.1005-3026.2014.10.009

• 材料与冶金 • 上一篇    下一篇

退火温度对含磷高强IF钢FeTiP析出行为的影响

张洁岑1,邸洪双1,蒋光炜1,2,曹宇1   

  1. (1东北大学 轧制技术及连轧自动化国家重点实验室, 辽宁 沈阳110819;2本溪钢铁(集团)有限责任公司 冷轧薄板厂, 辽宁 本溪117021)
  • 收稿日期:2014-04-23 修回日期:2014-04-23 出版日期:2014-10-15 发布日期:2014-05-19
  • 通讯作者: 张洁岑
  • 作者简介:张洁岑(1990-),女,重庆人,东北大学博士研究生;邸洪双(1958-),男,辽宁锦州人,东北大学教授,博士生导师.
  • 基金资助:
    国家重点基础研究发展计划项目(2011CB606306-2);中央高校基本科研业务费专项资金资助项目(N110607005).

Effect of Annealing Temperature on FeTiPType Precipitate in PAdded IF High Strength Steel

ZHANG Jiecen1, DI Hongshuang1, JIANG Guangwei1,2, CAO Yu1   

  1. 1. State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China; 2. Cold Rolling Mill, Benxi Iron & Steel Co., Ltd., Benxi 117021, China.
  • Received:2014-04-23 Revised:2014-04-23 Online:2014-10-15 Published:2014-05-19
  • Contact: DI Hongshuang
  • About author:-
  • Supported by:
    -

摘要: 通过模拟罩式退火过程,研究了含磷高强IF钢中FeTiP粒子在退火过程中的析出行为,利用透射电镜选区衍射并结合能谱分析,确定了FeTiP的晶体结构.结果表明:650℃退火试样中只含有少量FeTiP,随着退火温度的升高,FeTiP数量明显增加,其大量分布于晶内及晶界处,且晶界处析出物尺寸明显大于晶内析出物.当退火温度升高到800℃时,FeTiP完全溶解,因此在整个基体无法检测到FeTiP.FeTiP的溶解消除了其对再结晶的阻碍作用,最终获得高强度{111}取向再结晶组织,从而提高高强IF钢成形的性能.FeTiP具有斜方晶体结构,且析出物中Nb元素的存在(含Nb原子可表达为Fe(Ti,Nb)P)不会引起晶体结构的改变.

关键词: 高强IF钢, 退火温度, FeTiP, 晶体结构, 织构

Abstract: A systematic and detailed characterization of FeTiPtype precipitate, as a function of annealing temperature, was studied for a batchannealed Padded interstitial free high strength steel (IFHS). The results showed that a small number of FeTiP is observed at 650 ℃ and it increases dramatically with the increase of annealing temperature. FeTiP distributes within grains and at grain boundaries, but the size of intragranular FeTiP is found to be significantly smaller than that at grain boundary. FeTiP is totally dissolved and can not be detected at 800 ℃. The absence of FeTiP eliminates its inhibition effect on recrystallization and a high intensity {111} recrystallization texture is obtained, which improves the formability of IFHS. FeTiP is orthorhombic structure, and the enrichment of Nb in FeTiP precipitates does not alter the crystal structure of FeTiP.

Key words: interstitial free high strength steel, annealing temperature, FeTiP, crystal structure, texture

中图分类号: