Effect of Cold Rolling Deformation on Microstructure and Mechanical Properties of Solution-treated 2195 Al-Li Alloy

doi:10.12068/j.issn.1005-3026.2023.02.007

Abstract

Abstract: The extruded and solution-treated plates of 2195 Al-Li alloy were cold rolled by the reduction of 5%~25% followed by an artificially aging process， and then the effect of cold rolling deformation on its microstructure and mechanical properties were studied through microstructure analysis and tensile test. The results show that the 45° shear bands begin to appear among some fibrous structures in the thickness direction of the plate after the reduction reaches 20%. Furthermore， the bands can be distributed in the whole thickness of the plate when the reduction increases to 25%. After aging treatment(155℃ for 28h)， the yield， tensile strength and final elongation of the cold-rolled plates firstly increase and then decrease with the reduction increase. When the reduction is 10%， the yield， tensile strength and final elongation of the plate reach their maximum values of 575MPa， 604MPa and 13.7%， respectively. After aging， the yield-tensile strength ratio of the sample increases from 90.8% to 97.4% with the reduction from 0 to 20%， and then slightly decreases to 97.1% with further increasing reduction to 25%. Therefore， for the extruded and solution-treated 2195 Al-Li alloy plate， the reduction of cold rolling should be controlled around 10%.

Key words: 2195 Al-Li alloy;solid solution; cold rolling deformation; aging; mechanical properties

CLC Number:

TG166.3

ZUO Yu-bo， LING Fang， HAN You， ZHU Qing-feng. Effect of Cold Rolling Deformation on Microstructure and Mechanical Properties of Solution-treated 2195 Al-Li Alloy[J]. Journal of Northeastern University(Natural Science), 2023, 44(2): 199-205.

References

[1]Eswara N E，Gokhale A，Wanhill R J H. Aluminum-lithium alloys:processing，properties，and applications［M］.Oxford:Butterworth-Heinemann，2013.
[2]Bruch C A.The effect of plastic deformation on the age-hardening of duralumin［D］.Cambridge:Massachusetts Institute of Technology，1938.
[3]Kaufman J G.Introduction to aluminum alloys and tempers［M］.Cleveland:ASM International，2000.
[4]Broek D，Bowles C Q.Effect of precipitate size on crack propagation and fracture of an Al-Cu-Mg alloy［J］.Journal of the Japan Institute of Metals，1971，99:255-257.
[5]Murakami Y，Kawano O.Effects of cold working on the aging of Al-Cu alloy ［J］.Light Metal，1959，10(2):11-21.
[6]Murakami Y，Kawano O.Effects of plastic deformation on aging in ternary aluminium alloys ［J］.Transactions of the Japan Institute of Metals，1960，1(1):27-32.
[7]Anderson S J，Zandbergen H W，Jansen J，et al.Aluminium alloys:their physical and mechanical properties［J］.Acta Materialia，1998，46(9):3283-3298.
[8]Lee E W，Frazier W E.The effect of stretch on the microstructure and mechanical properties of 2090 Al-Li［J］.Scripta Metallurgica，1988，22(1):53-57.
[9]Cassada W A，Shiflet G J，Starke E A.The effect of plastic deformation on Al₂CuLi(T1) precipitation［J］.Metallurgical Transactions A，1991，22(2):299-306.
[10]Cassada W A，Shiflet G J，Starke E A.Mechanism of Al₂ CuLi(T1) nucleation and growth［J］.Metallurgical Transactions A，1991，22(2):287-297.
[11]Li G A，Ma Z，Jiang J T，et al.Effect of pre-stretch on the precipitation behavior and the mechanical properties of 2219 Al alloy［J］.Materials，2021，14(9):2101-2112.
[12]Tao J，Zhang L，Wu G，et al.Effect of heat treatment on the microstructure and mechanical properties of extruded Al-4Cu-1Li-0.4 Mg-0.4 Ag-0.18 Zr alloy［J］.Materials Science and Engineering:A，2018，717:11-19.
[13]Kim J D，Park J K.Effect of stretching on the precipitation kinetics of an Al-2.0 Li-2.8 Cu-0.5 Mg(-0.13 Zr)alloy［J］.Metallurgical and Materials Transactions A，1993，24(12):2613-2621.
[14]Kim N J，Lee E W.Effect of T1 precipitate on the anisotropy of Al-Li alloy 2090［J］.Acta Metallurgica et Materialia，1993，41(3):941-948.
[15]袁志山，陆政，谢优华，等.预变形对高强Al-Cu-Li-X铝锂合金组织和性能影响［J］.稀有金属材料与工程，2007(3):493-496.(Yuan Zhi-shan，Lu Zheng，Xie You-hua，et al.Effect of plastic deformation on microstructure and properties of high strength Al-Cu-Li-X aluminum-lithium alloy［J］.Rare Metal Materials and Engineering，2007(3):493-496.)
[16]向正武，李劲风，宁红，等.不同预变形量T8态时效2195铝锂合金微观组织与强度贡献［J］.宇航材料工艺，2021，51(4):140-146.(Xiang Zheng-wu，Li Jin-feng，Ning Hong，et al.Microstructure and strength contribution of T8-aged 2195 Al-Li alloy with different pre-stretching［J］.Aerospace Materials and Technology，2021，51(4):140-146.)
[17]都昌兵，熊纯，官瑞春，等.预拉伸对X2A66铝锂合金时效析出行为以及力学性能的影响［J］.航空材料学报，2020，40(5):29-37.(Du Chang-bing，Xiong Chun，Guan Rui-chun，et al.Effect of prestretching on the precipitation behavior and mechanical properties of X2A66 aluminum alloy［J］.Journal of Aeronautical Materials，2020，40(5):29-37.)
[18]邓燕君，黄光杰，曹玲飞，等.预变形对Al-Cu-Li-Mn-Zr合金的第二相析出及力学性能的影响［J］.材料导报，2018，32(4):569-573.(Deng Yan-jun，Huang Guang-jie，Cao Ling-fei，et al.Effect of pre-deformation on the precipitation behavior and mechanical property of Al-Cu-Li-Mn-Zr alloy［J］.Materials Review，2018，32(4):569-573.)
[19]张新明，贾寓真，刘玲，等.冷轧预变形对2519A铝合金时效析出的影响［J］.中南大学学报(自然科学版)，2011，42(1):46-50.(Zhang Xin-ming，Jia Yu-zhen，Liu Ling，et al.Effects of cold-pre-rolling reduction on precipitation of 2519A aluminum alloy plate［J］.Journal of Central South University(Natural Science Edition)，2011，42(1):46-50.)
[20]李慧中，梁霄鹏，陈明安，等.冷轧变形量对2519铝合金组织与力学性能的影响［J］.材料热处理学报，2008(2):86-89.(Li Hui-zhong，Liang Xiao-peng，Chen Ming-an，et al.Effect of cold rolling reduction on microstructure and mechanical property of 2519 aluminum alloy［J］.Transactions of Materials and Heat Treatment，2008(2):86-89.)
[21]Lu Y，Wang J，Li X，et al.Effects of pre-deformation on the microstructures and corrosion behavior of 2219 aluminum alloys［J］.Materials Science and Engineering:A，2018，723:204-211.
[22]Adcock F.The internal mechanism of cold-work and recrystallization in cupro-nickel［J］.Journal of the Japan Institute of Metals，1922，27:73-92.
[23]Mathur P S，Backofen W A.Mechanical contributions to the plane-strain deformation and recrystallization textures of aluminum-killed steel［J］.Metallurgical Transactions，1973，4(3):643-651.
[24]Huang H，Jiang F，Zhou J，et al.Effects of Al₃(Sc，Zr)and shear band formation on the tensile properties and fracture behavior of Al-Mg-Sc-Zr alloy［J］.Journal of Materials Engineering and Performance，2015，24(11):4244-4252.
[25]Wang Y，Xin Y，Yu H，et al.Formation and microstructure of shear bands during hot rolling of a Mg 6Zn 0.5 Zr alloy plate with a basal texture［J］.Journal of Alloys and Compounds，2015，644:147-154.
[26]Zakharov V V，Rostova T D.Shear bands in aluminum alloys containing scandium and lithium［J］.Metal Science & Heat Treatment，1996，38(4):163-167.
[27]Baumann S F，Williams D B.A new method for the determination of the precipitate-matrix interfacial energy［J］.Scripta Metallurgica，1984，18(6):611-616.
[28]Williams D B，Edington J W.The precipitation of δ′(Al3Li)in dilute aluminium-lithium alloys［J］.Metal Science，1975，9(1):529-532.
[29]Ceresara S，Giarda A，Sanchez A.Annealing of vacancies and ageing in Al-Li alloys［J］.Philosophical Magazine，1977，35(1):97-110.
[30]Dorin T，de Geuser F，Lefebvre W，et al.Strengthening mechanisms of T1 precipitates and their influence on the plasticity of an Al-Cu-Li alloy［J］.Materials Science and Engineering:A，2014，605:119-126.［31］Li J F，Ye Z H，Liu D Y，et al.Influence of pre-deformation on aging precipitation behavior of three Al Cu Li alloys［J］.Acta Metallurgica Sinica，2017，30(2):133-145.