Effects of high magnetic field annealing on recrystallization texture of cold-rolled IF steel sheet

Wu, Yan (1); Zhao, Xiang (1); He, Chang-Shu (1); Zuo, Liang (1)   

  1. (1) Key Laboratory for Anisotropy and Texture of Materials, Northeastern University, Shenyang 110004, China
  • Received:2013-06-22 Revised:2013-06-22 Online:2008-09-15 Published:2013-06-22
  • Contact: Wu, Y.
  • About author:-
  • Supported by:
    -

RichHTML

0

PDF (PC)

902

Abstract: The effects of high magnetic field annealing on the recrystallization texture in the initial stage of recrystallization in as-annealed interstitial-free (IF) steel sheet were investigated by the SEM-EBSD analysis. The annealing was conducted in a 12-tesla magnetic field at 650°C which was held for 0, 10 and 30 min separately to obtain the partially recrystallized microstructure in samples. It was found that the {111}<112> texture component, as compared with other {111} texture components, was favored by the applied high magnetic field in the initial stage of nucleation and growth.