Control Model of Effective Ti Content for Hearth Protection by TitaniumBearing Material

JIAO Kexin1,2, ZHANG Jianliang1,2, ZUO Haibin1,2, LIU Zhengjian1,2   

  1. 1 School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China; 2 State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China.
  • Received:2013-08-02 Revised:2013-08-02 Online:2014-08-15 Published:2014-04-11
  • Contact: ZUO Haibin
  • About author:-
  • Supported by:
    -

Abstract: The titaniumbearing material reduction behavior and the protection mechanism for a hearth were analyzed, based on which, the control model of the effective Ti content was established. The effective TiO2 content, critical Ti content with which TiC precipitated and the corresponding precipitation temperature could be calculated by the model according to the realtime parameters of the BF in the actual production in order to guide the production practice. Given the production parameters, the calculated results showed that the effective TiO2 content should be 08 wt%-10 wt%, and the Ti content in molten iron, in which the hearth could be effectively protected, should be 011 wt%-014 wt%. Furthermore, the influence of hot metal ingredients on the precipitation of TiC was analyzed.

Key words: blast furnace, hearth protection, TiO2 activity, Ti(C, N), effective Ti content, control model