NaCl溶液中20Cr9Ni5Co14不锈钢电化学腐蚀行为

文陈1， 许广兴2， 樊立伟3， 陈亚争2   

  1. (1. 北京航空航天大学 材料科学与工程学院， 北京100191; 2. 沈阳飞机设计研究院， 辽宁 沈阳110035;3. 中国人民解放军驻沈阳飞机工业(集团)有限公司 军事代表室， 辽宁 沈阳110034)
  • 收稿日期:2013-11-20 修回日期:2013-11-20 出版日期:2015-06-15 发布日期:2015-06-11
  • 通讯作者: 文陈
  • 作者简介:文陈(1985-)，男，湖南醴陵人，北京航空航天大学博士研究生.
  • 基金资助:
    国家自然科学基金资助项目(51171011).

Electrochemical Corrosion Behaviors of 20Cr9Ni5Co14 Stainless Steels in NaCl Solution

WEN Chen1， XU Guang-xing2， FAN Li-wei3， CHEN Ya-zheng2   

  1. 1. School of Material Science and Engineering， Beihang University， Beijing 100191， China; 2. Shenyang Aircraft Design & Research Institute， Shenyang 110035， China; 3. PLA Military Representative Office in Shenyang Aircraft Industries
  • Received:2013-11-20 Revised:2013-11-20 Online:2015-06-15 Published:2015-06-11
  • Contact: WEN Chen
  • About author:-
  • Supported by:
    -

RichHTML

0

PDF (PC)

703

摘要： 采用电化学极化技术(动电位极化技术、线性极化技术和循环极化技术)和交流阻抗技术研究了不同条件下20Cr9Ni5Co14超高强度不锈钢的电化学腐蚀行为，并采用扫描电镜对极化后腐蚀形貌进行了表征.结果表明，20Cr9Ni5Co14钢在3.5%(质量分数)NaCl溶液中出现钝化.随着NaCl浓度的升高，钝化现象消失，而自腐蚀电流密度从8.223×10-7A/cm2减小至1.129×10-7A/cm2；随着pH值的降低，20Cr9Ni5Co14钢的致钝电位和过钝化电位增加.在pH值高于3时，腐蚀产物膜具有良好的耐腐蚀性能而导致反应步骤成为控制步骤.而当pH值降低到2时，腐蚀产物溶解速度很快，金属界面发生腐蚀速率很大，浓差极化成为了控制步骤.对腐蚀形貌研究表明，20Cr9Ni5Co14钢在极化过程中出现点腐蚀，导致了材料的耐腐蚀性能下降.

关键词: 电化学极化, 交流阻抗, 20Cr9Ni5Co14, 不锈钢

Abstract: The corrosion behaviors of 20Cr9Ni5Co14 ultra high strength steel (USS) were studied by the electrochemical polarization methods (potentiodynamic polarization， linear polarization and cyclic polarization technologies) and alternating current impedance spectrum methods in different corrosion conditions， and after polarization the corrosion morphologies were characterized by Scanning Electron Microscopy(SEM). The results showed that the passivation phenomenon of 20Cr9Ni5Co14 steels appeared in 3.5wt.% NaCl solution while disappeared with the increase of NaCl concentration. The corrosion current also reduced from 8.223×10-7A/cm2 to 1.129×10-7A/cm2 with the increase of NaCl concentration. The passivation and transpassivation potentials of 20Cr9Ni5Co14 steels increased with the increase of hydrogen ion concentrations. When the pH value was higher than 3， the corrosion product film had excellent corrosion resistancewhich led the electrochemical polarization step as a dominated step， while the pH value decreased to 2， the corrosion products dissolution rate was fast， the corrosion rate of the interface of the metal surface and the solution was also fast， thus the polarization caused by concentration differences became the dominated step. Corrosion morphology studies showed that the corrosion of 20Cr9Ni5Co14 steels in the polarization process oriented from pitting corrosion， which leads to the reduction of corrosion resistance.

Key words: electrochemical polarization, electrochemical impedance spectroscopy, 20Cr9Ni5Co14, stainless steel