东北大学学报（自然科学版）

东北大学学报:自然科学版 ›› 2016, Vol. 37 ›› Issue (3): 338-342.DOI: 10.12068/j.issn.1005-3026.2016.03.008

• 材料与冶金 • 上一篇    下一篇

离心铸造高铅锡青铜合金摩擦磨损性能研究

刘越1， 陈超1， 吕文玲2   

  1. (1. 东北大学 材料科学与工程学院， 辽宁 沈阳110819； 2. 鞍钢重型机械有限责任公司， 辽宁 鞍山114021)
  • 收稿日期:2015-01-04 修回日期:2015-01-04 出版日期:2016-03-15 发布日期:2016-03-07
  • 通讯作者: 刘越
  • 作者简介:刘越(1960- )，男，辽宁沈阳人，东北大学教授.
  • 基金资助:
    辽宁省科技创新重大专项(201404001)； 沈阳市科技计划项目(F13-316-18).

Study on Friction and Wear Properties of High Lead Tin-Bronze Alloy by Centrifugal Casting

LIU Yue1， CHEN Chao1， LYU Wen-ling2   

  1. 1. School of Materials Science & Engineering， Northeastern University， Shenyang 110819， China; 2. Angang Heavy Machinery Co.， Ltd.， Anshan 114021， China.
  • Received:2015-01-04 Revised:2015-01-04 Online:2016-03-15 Published:2016-03-07
  • Contact: LIU Yue
  • About author:-
  • Supported by:
    -

RichHTML

0

PDF (PC)

855

摘要： 采用离心铸造方法制备了高铅锡青铜(ZCuPb22Sn1.5)合金，研究了载荷和摩擦速度对其摩擦磨损性能的影响及摩擦磨损机理.研究发现:在0.05m/s摩擦速度下，随着载荷的增加，高铅锡青铜合金摩擦系数减小，磨损率增加，当载荷增加到120N后，摩擦系数趋于稳定；在100N载荷下，随着摩擦速度的增加，摩擦系数逐渐减小，磨损率增加，摩擦速度增加到0.10m/s以后，摩擦系数迅速减小，到0.20m/s以后摩擦系数趋于稳定；当继续增加载荷和摩擦速度时，由于铅润滑膜的破坏而增加了磨损率.在摩擦磨损过程中容易在摩擦表面形成软质铅润滑膜从而起到耐磨作用.

关键词: 高铅锡青铜, 离心铸造, 摩擦磨损, 载荷, 黏着磨损

Abstract: High lead tin-bronze (ZCuPb22Sn1.5) was produced by centrifugal casting method. The friction and wear properties of the materials were investigated at fixed loads and friction speed，and the wear mechanisms were also analyzed. The results showed that the wear rate increases and the friction coefficient decreases with the increasing the load， the friction coefficient decreases rapidly and then trends to be stable as the loads increases to 120N when the friction speed is below 0.05m/s. Similarly， at the loads of 100N the wear rate increases and the friction coefficient decreases with the increase of the friction speed when the friction speed increases to 0.10 m/s， the friction coefficient decrease rapidly， and then trends to be stable as the friction speed increases to 0.20m/s. Then， with the increase of the fixed loads and friction speed， the solid lubrication film is damaged， the wear of the materials is severe and the wear rate unstably increases. In the process of friction and wear the Pb solid lubrication film on the worn surface is stable， and the materials have good antifriction and lower wear.

Key words: high lead tin-bronze, centrifugal casting, friction and wear resistance, load, adhesion wear

中图分类号: