多道次搅拌摩擦加工对5083-O铝合金组织性能的影响

doi:10.12068/j.issn.1005-3026.2014.10.013

东北大学学报:自然科学版 ›› 2014, Vol. 35 ›› Issue (10): 1422-1426.DOI: 10.12068/j.issn.1005-3026.2014.10.013

多道次搅拌摩擦加工对5083-O铝合金组织性能的影响

陈雨¹，李晓华²，付明杰²，丁桦¹

(1 东北大学材料与冶金学院，辽宁沈阳110819；2 中航工业北京航空制造工程研究所，北京100024)

收稿日期:2013-11-18 修回日期:2013-11-18 出版日期:2014-10-15 发布日期:2014-05-19
通讯作者: 陈雨
作者简介:陈雨(1989-)，男，辽宁沈阳人，东北大学博士研究生；丁桦(1958-)，女，安徽合肥人，东北大学教授，博士生导师.
基金资助:
航空支撑项目(61901110301).

Effect of Multipass Friction Stir Processing on Microstructures and Mechanical Properties of 5083O Aluminum Alloy

CHEN Yu¹， LI Xiaohua²， FU Mingjie²， DING Hua¹

1. School of Materials & Metallurgy， Northeastern University， Shenyang 110819， China； 2. AVIC Beijing Aeronautical Manufacturing Technology Research Institute， Beijing 100024， China.

Received:2013-11-18 Revised:2013-11-18 Online:2014-10-15 Published:2014-05-19
Contact: DING Hua
About author:-
Supported by:
-

摘要/Abstract

摘要： 在不同轴肩直径、搅拌头转速和搅拌头行进速度下，对27mm厚5083-O铝合金进行了多道次搅拌摩擦加工(multipassfrictionstirprocessing)，搭接率为100%，共进行3道次搅拌摩擦加工.研究结果表明，加工区由细小的再结晶组织组成；随着加工道次的增加，加工区内部缺陷体积减少，晶粒进一步细化，析出相细化并均匀分布，力学性能提高，加工区最高抗拉强度可达360MPa，延伸率也优于母材；其中，第二道次加工对材料组织和性能的影响最为明显.

关键词: 多道次, 搅拌摩擦加工, 5083-O铝合金, 微观组织, 力学性能

Abstract: Multipass friction stir processing (3pass FSP with 100% overlap) was conducted under different diameters of shoulders， rotation speeds and travel speeds to investigate the effect of processing parameters on the microstructures and the mechanical properties of 5083O aluminum alloy. The results showed that the fine and dynamically recrystallized grains are observed in the FSP zone. With increasing the number of passes， the grain size and the tunnel defects decrease， the second phase particles are refined and distributed uniformity， the ultimate tensile strength reaches up to 360 MPa， and the elongation is higher than that of the base metal. The effect of the 2ndpass on the microstructures and mechanical properties is most obvious.

Key words: multipass, friction stir processing, 5083O aluminum alloy, microstructure, mechanical property

中图分类号:

TG1462

陈雨，李晓华，付明杰，丁桦. 多道次搅拌摩擦加工对5083-O铝合金组织性能的影响[J]. 东北大学学报:自然科学版, 2014, 35(10): 1422-1426.

CHEN Yu， LI Xiaohua， FU Mingjie， DING Hua. Effect of Multipass Friction Stir Processing on Microstructures and Mechanical Properties of 5083O Aluminum Alloy[J]. Journal of Northeastern University Natural Science, 2014, 35(10): 1422-1426.

参考文献

［1］Mishra R S，Mahoney M W，McFadden S X，et al.High strain rate superplasticity in a friction stir processed 7075 Al alloy［J］.Scripta Materialia，1999，42(2):163-168.
[2]Hao H L，Ni D R，Huang H，et al.Effect of welding parameters on microstructure and mechanical properties of friction stir welded AlMgEr alloy［J］.Materials Science and Engineering A，2013，559:889-896.
[3]Hirata T，Oguri T，Hagino H，et al.Influence of friction stir welding parameters on grain size and formability in 5083 aluminum alloy［J］.Materials Science and Engineering A，2007，456:344-349.
[4]Cui G R，Ma Z Y，Li S X.The origin of nonuniform microstructure and its effects on the mechanical properties of a friction stir processed AlMg alloy［J］.Acta Materialia，2009，57:5718-5729.
[5]Yoon S O，Kang M S，Nam H B，et al.Friction stir butt welding of A5052O aluminum alloy plates［J］.Transactions of Nonferrous Metals Society of China，2012，22:619-623.
[6]Sato Y S，Urata M，Kokawa H.Parameters controlling microstructure and hardness during frictionstir welding of precipitationhardenable aluminum alloy 6063［J］.Metallurgical and Materials Transactions A，2002，33(3):625-635.
[7]Kim Y G，Fujii H，Tsumura T，et al.Three defects types in friction stir welding of aluminum die cast alloy［J］.Materials Science and Engineering A，2006，415:250-254.
[8]Jata K V，Semiatin S L.Continuous dynamic recrystallization during friction stir welding of high strength aluminum alloys［J］.Scripta Materialia，2000，43(8):743-749.
[9]Kwon Y J，Loureiro A.Microstructure and mechanical properties of friction stir welds in aluminum alloys 2024T3，5083O and 6063T6［J］.Materials Science Forum，2006，516(6):697-701.一位数()
[10]二位数()

[1]	温雪龙，王承宝，刘文博，任海洋. 选区激光熔化FeCoNiCr系高熵合金微观组织的实验研究[J]. 东北大学学报（自然科学版）, 2023, 44(4): 536-543.
[2]	邸洪双，柯浩鹏，张天宇. 多步热处理对含Cu中碳低合金钢组织与性能的影响[J]. 东北大学学报（自然科学版）, 2023, 44(3): 340-348.
[3]	左玉波，凌放，韩友，朱庆丰. 固溶后冷轧变形量对2195铝锂合金组织和力学性能的影响[J]. 东北大学学报（自然科学版）, 2023, 44(2): 199-205.
[4]	支卫军，姚赞，姜周华. 高碳镀锌钢丝的组织演变及对扭转性能的影响[J]. 东北大学学报（自然科学版）, 2023, 44(1): 49-54.
[5]	田妮，张耀中，周轶然，秦广华. Zr对Al-10Zn-2.5Mg-1.6Cu合金板材组织与性能的影响[J]. 东北大学学报（自然科学版）, 2022, 43(7): 951-958.
[6]	赵宇辉，高孟秋，赵吉宾，贺晨. 增减材复合制造WC颗粒增强316L不锈钢材料组织性能[J]. 东北大学学报（自然科学版）, 2022, 43(2): 197-205.
[7]	王胤，李勇，钱晓明，张博四. 真空离心铸造冷却速率对7055铝合金组织和力学性能的影响[J]. 东北大学学报（自然科学版）, 2022, 43(12): 1769-1776.
[8]	姚云龙，修世超，孙聪，洪远. 基于40Cr高温动态力学性能的磨削表面动态再结晶行为[J]. 东北大学学报（自然科学版）, 2021, 42(8): 1120-1126.
[9]	张广泰，吴锐，李雪藩，阿迪力·赛买提. 老化-荷载作用下叠层轮胎隔震垫时变力学性能[J]. 东北大学学报（自然科学版）, 2021, 42(8): 1180-1186.
[10]	高彩茹，屈兵兵，田余东，杜林秀. 回火温度对在线淬火Q690q桥梁钢显微组织和力学性能的影响[J]. 东北大学学报（自然科学版）, 2021, 42(7): 927-933.
[11]	朱成林，高秀华，王明明，宋丽英. 淬火温度对12Cr14Ni2不锈结构钢组织及力学性能的影响[J]. 东北大学学报（自然科学版）, 2021, 42(6): 781-788.
[12]	董硕，沙松，蒙世仟，荣冠. 液氮冷却作用下三类高温岩石力学性能试验研究[J]. 东北大学学报（自然科学版）, 2021, 42(11): 1591-1599.
[13]	蔡志辉，文光奇，韩阿康，张开华. 调质工艺对V微合金油井管用钢力学性能的影响[J]. 东北大学学报（自然科学版）, 2021, 42(10): 1414-1420.
[14]	鲍君峰，于月光，贾成厂. ZrO₂添加量对等离子放电烧结制备WC-6Co组织和性能的影响[J]. 东北大学学报（自然科学版）, 2021, 42(1): 43-48.
[15]	王明明，高秀华，杜林秀，张大征. V-N微合金化X80抗大变形管线钢的组织与力学性能[J]. 东北大学学报:自然科学版, 2020, 41(6): 801-806.

多道次搅拌摩擦加工对5083-O铝合金组织性能的影响

Effect of Multipass Friction Stir Processing on Microstructures and Mechanical Properties of 5083O Aluminum Alloy

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价