WANG Chao, LI Yuanyuan, WANG Zhaodong, WANG Guodong. Influence of Rolling and Cooling Process on Mechanical Properties of a Low Alloy Quenched and Tempered Steel[J]. Journal of Northeastern University, 2013, 34(6): 815-819.
[1] Wang Z D,Kang J,Lu F,et al.Study on quenching and tempering process of Q960 high strength steel for construction machinery[J].Journal of Iron and Steel Research,International,2011,18(S1/1):432/436. [2] Adamczyk J,Opiela M.Influence of the thermomechanical treatment parameters on the inhomogeneity of the austenite structure and mechanical properties of the CrMo steel with Nb,Ti,and B microadditions[J].Journal of Materials Processing Technology,2004,157/158:456/461. [3] Yu W,Qian Y J,Wu H B,et al.Effect of heat treatment process on properties of 1000MPa ultrahigh strength steel[J].Journal of Iron and Steel Research,International,2011,18:64/69. [4] 赵琳,张旭东,陈武柱.800MPa级低合金钢焊接热影响区韧性的研究[J].金属学报,2005,41(4):392/396.(Zhao Lin,Zhang Xudong,Chen Wuzhu.Toughness of heataffected zone of 800MPa grade low alloy steel[J].Acta Metallurgica Sinica,2005,41(4):392/396.) [5] Furuhara T,Kikumoto K,Saito H,et al.Phase transformation from finegrained austenite[J].ISIJ International,2008,48(8):1038/1045. [6] Morito S,Yoshida H,Maki T,et al.Effect of block size on the strength of lath martensite in low carbon steels[J].Materials Science and Engineering A,2006,438/439/440:237/240. [7] Wang C F,Wang M Q,Shi J,et al.Effect of microstructural refinement on the toughness of low carbon martensitic steel[J].Scripta Materialia,2008,58:492/495. [8] Speich G R,Leslie W C.Tempering of steel[J].Metallurgical Transactions,1972,3:1043/1054. [9] Pesicka J,Dronhofer A,Eggeler G.Free dislocations and boundary dislocations in tempered martensite ferritic steels[J].Materials Science and Engineering A,2004,387/388/389:176/180.